I would normally go for a single run Dean.
If trying to to fill wide gaps you don't really have any alternative to trigger blipping .... Well that is bar, trying vertical down run
You can get some decent penetration by pulsing if you up the current a fair bit ( A bit like you should for a nice hot tack weld )
Is there a particular joint that is causing you a problem ?