Smoke on high temp paint
Hi,
I have started my engine today. First time with the exhaust manifold I modified. I painted this manifold and the tube with black high temperature paint (650°C). When I ran the engine today, when it started to heat up, the manifold was smoking a lot from everywhere, a bit like if the painting was burning. I preferred to stop rather than wait and set up a fire. Is it normal to have smoke on the paint the first time it is used? Perhaps it is smoking a lot at the beginning, and then stabilizes after a while? Or did I use a wrong paint, 650°C not being enough? Thank you for your help.
__________________
Sylvain Pictures of my completed Roadster https://www.flickr.com/photos/994983...7646799525542/ Build blog: http://vouchtroadster.blogspot.se/ https://cafrazx550.blogspot.com/ |
#2
|
||||
|
||||
Did you fully clean and degrease the steel or use a primer under the high temp paint?
__________________
Website http://www.talonmotorfabrication.co.uk/ Direct email phil@talonmotorfabrication.co.uk talonmotorfabrication@gmail.com Mobile office hours 07514098334 |
#3
|
||||
|
||||
Actually, after the electrolysis, I washed it with soap, rinsed it and dried it (heat gun + pressured air from the compressor). But I did not specifically degreased with a degreasing agent (except soap )
But no primer. The weird thing is that it was smoking (and smelling) a lot when the engine was running, but now, there is no trace of anything, no bubbles or burn paint on the parts, nothing... But I guess by your reply that there is something wrong anyway , no? Should I insist and let is smoke until it stops, hopping that the high temp paint wont be damaged ? Thanks
__________________
Sylvain Pictures of my completed Roadster https://www.flickr.com/photos/994983...7646799525542/ Build blog: http://vouchtroadster.blogspot.se/ https://cafrazx550.blogspot.com/ |
#4
|
||||
|
||||
650 deg is not enough. gasses leaving the head is often 800 deg or more depending on the engine, most HT paints for exhausts are 1200 deg.
__________________
Be Lucky, Mike. |
#5
|
||||
|
||||
Thanks Mike,
Actually you are right, 650°C is not enough for an exhaust manifold, and it is more adapted to brakes. I couldn't find 1200°C, but I know where to get 800°C paint which seems to be the most popular one for exhaust parts. However, I have read some forum here in Sweden about the paint I used, and it looks like this paint has to be «*cooked*» to be hardened after being applied. People put their parts in an oven, ore use a heat gun. Some other say that running the engine for exhaust parts and letting it cool down id the way to go, and will do the hardening job. That is what I did yesterday. After 10-15 minutes of running the engine, the manifold stopped smoking, and the paint still look nice and hasn't been affected by the heat. I'll have another run today from cold engine, and see what happen, but I think I am going to leave it like that if everything looks OK. Thank you for the inputs.
__________________
Sylvain Pictures of my completed Roadster https://www.flickr.com/photos/994983...7646799525542/ Build blog: http://vouchtroadster.blogspot.se/ https://cafrazx550.blogspot.com/ |
#6
|
||||
|
||||
I remember that "few" years ago I used exhaust paint on 2T motorbike and the result was similar to yours - lot of smoke. But after first smoking ride it was OK. So should be OK with your exhaust
__________________
Lucas ZX9R BEC Haynes Roadster - build cost so far: £1125 My build thread "Whatever you can do or dream you can, begin it. Boldness has genius, power, and magic in it." J.W.Goethe |
#7
|
|||
|
|||
Sperex was the paint to use,dont know if still available.
__________________
Cost : Little as possible. Thanks : To those who by their generosity my build has progressed. Its a handmade sports car not a flaming kit car !!! If at first you dont succeed,avoid skydiving... No parachute require to freefall,only if you want to do it twice. |
#8
|
|||
|
|||
A lot of high temp paint will only cure if brought up to temperature.
Shutting off early may have prevented that, so fire it up again and let it run and get hot. It looks far worse than it really is. Also everything else related to the engine will also be burning off, any oil protectorate left inside the exhaust pipes will also burn off, etc. Some first time fire ups can be quite a smoke show but harmless, it will burn off and then your car will be fine. It is normal the first time out. Al
__________________
1969 Amx 2004 Passat 1.8T 5Spd 4Motion Haynes Modified Super 7 3.4L V6 www.lotussuper7replica.com/ |
#9
|
||||
|
||||
Heh! Just a plain stainless manifold of mine smoked like crazy during the first firing. http://youtu.be/NZDFKbk8q_A?t=1m
__________________
Albert Haynes Roadster FAQ | Haynes Builder Locations Gallery, build thread in Lithuanian / via Google Translate. |
#10
|
||||
|
||||
Just a small follow up on this thread.
The collector has stopped smoking after a while as expected. But 650°C paint is definitely not enough for a collector. The painting is starting to get off in small chips now... I will need to repaint the collector with a proper 1200°C paint as Mike said (if I can find that here, which is not sure...) Thanks for the help and inputs
__________________
Sylvain Pictures of my completed Roadster https://www.flickr.com/photos/994983...7646799525542/ Build blog: http://vouchtroadster.blogspot.se/ https://cafrazx550.blogspot.com/ |