Welding with Argon/CO2 vs CO2

		Haynes Forums > Haynes Roadster Forums > Chassis
Welding with Argon/CO2 vs CO2

#11

25th November 2011, 11:25 PM

Trophy Blue Trophy Blue is offline

Member

Join Date: Mar 2007

Location: West Cornwall

Posts: 77

CO2 is added to pure argon to increase penetration, CO2 on its own will burn into the parent material, but will produce a brittle weld.